氧化锌纳米材料的机械法制备及其光学性能研究

采用滚压振动磨在干法室温状态下大批量制备了氧化锌纳米材料,分别利用X射线衍射仪(XRD)、透射电镜(TEM)和原子力显微镜(AFM)对样品晶体结构和形貌进行了表征.结果表明,ZnO纳米颗粒平均粒径约为60 nm,材料结晶良好,无杂质.室温下光致发光(PL)谱显示,在390 nm处有近带边紫外发射峰,这属于激子态发光;同时,在510 nm处有较弱的绿光发射峰,而强度最强的是位于648 nm处的红光发射峰,这两种发射属于表面缺陷态发光.UV-Vis吸收光谱表明,产物在紫外区有很强的紫外吸收,吸收峰出现了蓝移现象,这种蓝移验证了材料存在键断裂等表面缺陷态.Raman光谱表明非极性光学声子模位于437.6com-1处,纵向光学模(LO)峰位于583.6 cm-1处.

Fabrication of ZnO nanoparticles by roller vibration milling and their optical properties

Large scale manufacturing of ZnO nanoparticles at room temperature was reported.The as-synthesized particles and their optical performance were characterized by XRD,TEM,AFM,PL,UV-vis absorption spectra and Raman spectra.The synthesized ZnO nano-particles,the size of which is about 60 nm,have good crystal structure,and are free of impurity.Room temperature PL shows an ultraviolet band emission peaked at around 390 nm corresponding to the near band-edge emission and a green band peaked at around 510 nm.The mo...